Nanoparticles as a control for cyanobacterial bloom

Vật liệu nano đóng vai trò kiểm soát sự bùng nổ của vi khuẩn lam

Abstract

This study aims to investigate the toxicity of copper material synthesized by chemical reduction method and effects of environmental variables on growth of phytoplankton community (dominated by Microcystis genus) in the Tien eutrophic lake, Hanoi, Vietnam. The variables analyzed include: physical (pH and Turbidity), chemical (content of NH4+, PO43- and copper metal), biological (con- tent of Chlorophyll-a, cell density). The characteristic of nanomaterial was confirmed by using UV- visible spectrophotometer, XRD, SEM and TEM methods. The CuNPs showed they spherical form and uniform size about 20-40 nm. The experimental results showed that the treated with CuNPs inhibition on growth against phytoplankton after 8 days. The cell density of phytoplankton commu- nity and Microcystis genus in samples exposure with CuNPs declined after 8 days from 647.037 and 467.037 down to 381.111 and 202.592, respectively.

Mục đích của nghiên cứu này là khảo sát độc tính của vật liệu nano đồng được tổng hợp bằng phương pháp khử hóa học và ảnh hưởng của các yếu tố môi trường đến sinh trưởng và phát triển của quần xã thực vật nổi (chủ yếu là chi Microcystis) trong nước hồ Tiền phú dưỡng, tại Hà Nội, Việt Nam. Các thông số phân tích bao gồm: thủy lý (pH và độ đục), hóa học (hàm lượng amoni, photphat và hàm lượng đồng kim loại), sinh học (hàm lượng chất diệp lục, mật độ tế bào). Đặc trưng của vật liệu được xác định bằng các phương pháp quang phổ UV-VIS, XRD, SEM và TEM. Vật liệu nano đồng có dạng hình cầu, kích thước đồng nhất từ 20 đến 40 nm. Kết quả thử nghiệm sau 8 ngày cho thấy các mẫu có bổ sung vật liệu nano đồng ức chế sinh trưởng quần xã thực vật nổi ở nồng độ 1mg/l. Mật độ quần xã thực vật nổi và chi Microcystis trong mẫu xử lý với CuNPs đã giảm tương ứng sau 8 ngày từ 647.037 và 467.037 xuống còn 381.111 và 202.592.