Creating nano composite TiO2.Fe2O3/laterite material applying to treat arsenic compound in groundwater

Chế tạo vật liệu nano composite TiO2.Fe2O3/đá ong ứng dụng xử lý asen trong nước ngầm

Abstract

This article presents nano composite TiO₂.Fe₂O₃/laterite materials, which were successfully prepared by hydrometallurgical method. The materials were modified using urea as the nitrogen source. The particles size of the materials is from 20-30 nanometers. The obtained materials can not only absorb arsenic compounds but also enhance the ability of converting As (III) or As (V) into As^o, which is removed from solution. Arsenic removal efficiency of these materials is high. Using sunlight in a hydraulic retention time, about 180 minutes, the arsenic value at the inflow was about 10 mg/L but the outflow was negligible. Covering TiO₂.Fe₂O₃ nano on laterite have brought high economical efficiency, on one hand, it saved material and on the other hand, it can be continuously operated without the centrifugal separation of the nano material.

Bài báo này giới thiệu về phương pháp điều chế vật liệu nano TiO₂.Fe₂O₃ biến tính nitơ được phủ trên đá ong bằng phương pháp thủy luyện. Vật liệu nano thu được có kích thước 20-30 nm. Vật liệu thu được không những có khả năng hấp phụ các hợp chất của asen mà còn có khả năng khử As (III) hoặc As (V) thành Asokhi được chiếu sáng. Sử dụng ánh sáng mặt trời chiếu vào hệ thống xử lý trong thời gian 180 phút có thể loại bỏ được gần như hoàn toàn asen ra khỏi nước mặc dù hàm lượng đầu vào là 10 mg/l. Việc phủ vật liệu TiO₂.Fe₂O₃ nano lên đá ong đã mang lại hiệu quả kinh tế cao, một mặt nó tiết kiệm được vật liệu, mặt khác, vật liệu có thể sử dụng một cách liên tục mà không cần phải tách bằng phương pháp ly tâm.